Ba0.06(Na,Bi)0.94Ti1−x(Ni1/3Nb2/3)xO3 ceramics: X-ray diffraction and infrared spectroscopy studies

Non-lead ceramic samples of Ba0.06(Na0.5Bi0.5)0.94Ti1-x(Ni1/3Nb2/3)xO3; 0 ≤ x ≤ 1.0 were prepared by standard high temperature ceramic synthesis method. Rietveld refinements of X-ray diffraction data of these ceramics were carried out using FullProf software and determined their crystal symmetry, space group and unit cell dimensions. Rietveld refinement revealed that Ba0.06(Na0.5Bi0.5)0.94TiO3 has a monoclinic structure with space group P4/m while B0.06(Na0.5Bi0.5)0.94(Ni1/3Nb2/3)O3 has tetragonal (pseudo-cubic) structure with space group P4/mmm. Partial replacement of Ti4+ ion by pseudo-cation (Ni1/33+Nb2/35+)4+ resulted in the change of unit cell structure from monoclinic to tetragonal. SEM studies were carried out in order to access the quality of the prepared ceramics which showed a change in grain sizes with the increase of (Ni1/33+Nb2/35+)4+ content. FTIR spectra confirmed the formation of perovskite type solid solutions.