Preferential intergranular oxidation as a potential degradation mechanism for Alloy X-750 CANDU spacers

Oxidation experiments on Alloy X-750 were performed in reducing CO-CO2 mixtures to assess the possibility of preferential intergranular oxidation (PIO) in relation to CANDU garter-spring spacers. The testing environments simulate hypothetical off-chemistry scenarios, promoting the oxidation of the alloying elements, but not Ni. Surface and cross-section microscopy corroborated by Auger electron spectroscopy confirmed the occurrence of internal and intergranular oxidation in Alloy X-750, accompanied by Ni nodule expulsion to the surface. Results are qualitatively similar to observations in Alloy 600 exposed to 480°C hydrogenated steam, used as an accelerated environment for primary water stress corrosion cracking (PWSCC) testing.