Growth of austenite from as-quenched martensite during intercritical annealing in an Fe–0.1C–3Mn–1.5Si alloy

The growth of austenite from as-quenched martensite during intercritical annealing was studied in a quaternary Fe–0.1C–3Mn–1.5Si alloy. Fine austenite grains either grew from interlath-retained austenite films or were newly nucleated at lath and martensite packet boundaries. Both types grew to a size comparable to the width of the martensite lath. It was found both metallographically and by dilatometry that the austenite grew to an amount in …