Phosphorescence in Mn4+-DopedR+/R2+Germanates (R+= Na+or K+,R2+= Sr2+)
Journal Articles
Overview
Research
Identity
Additional Document Info
View All
Overview
abstract
Single crystals of three new compounds, Na0.36Sr0.82Ge4O9 (1, proposed composition), Na2SrGe6O14 (2), and K2SrGe8O18 (3), were obtained and characterized using single-crystal X-ray diffraction. Their structures contain three-dimensional (3D) anionic frameworks built from GeO4 and GeO6 polyhedra. The presence of octahedral Ge4+ sites makes the new phases suitable for Mn4+ substitution to obtain red-emitting phosphors with a potential application for light conversion. Photoluminescence properties of Mn4+-substituted Na2SrGe6O14 (2) and K2SrGe8O18 (3) samples were studied over a range of temperatures, and red light photoluminescence associated with the electronic transitions of tetravalent manganese was observed. The Na2SrGe6O14 (2) phase was also substituted with Pr3+ on the mixed Na-Sr site similar to the previously studied Na2CaGe6O14:Pr3+. The red emission peak of the Pr3+ activator occurs at a shorter wavelength (610 nm) compared to that of Mn4+ (662-663 nm). Additionally, second harmonic generation (SHG) data were collected for the noncentrosymmetric Na2SrGe6O14 (2) phase, indicating weak SHG activity. Diffuse reflectance spectroscopy and density of states calculations were performed to estimate the band gap values for pristine Na2SrGe6O14 (2) and K2SrGe8O18 (3) phases.