Study on the Toughness of X100 Pipeline Steel Heat Affected Zone

Microstructure-property correlation of heat affected zone (HAZ) in X100 longitudinal submerged arc welding (LSAW) real weld joint was studied in this paper. Coarse grained (CG) HAZ and intercritically reheated coarse grained (ICCG) HAZ were characterized by optical microscope (OM), electron backscattered diffraction (EBSD). The microstructure of CGHAZ is mostly composed of granular bainite with low density of high angle boundaries (HAB). Prior austenite grain size is ~80μm. In ICCGHAZ, coarse prior austenite grains were decorated by coarse necklacing martensite-austenite (M-A) constituents. Different layers were observed within M-A constituent, which may be martensite and austenite layers. Charpy absorbed energy of two different HAZ regions (ICCGHAZ containing and non-containing regions) was recorded using instrumental Charpy impact test machine. The results showed that the existence of ICCGHAZ resulted in the sharp drop of Charpy absorbed energy from 180J to 50J, while the existence of only CGHAZ could still lead to good toughness. The fracture surface was ~60% brittle in the absence of ICCGHAZ, and 100% brittle in the presence of ICCGHAZ in the impact tested samples. The underlying reason is the microstructure of ICCGHAZ consisted of granular bainite and upper bainite with necklace-type M-A constituent along the grain boundaries. Cleavage fracture initiated from M-A constituent, either through cracking of M-A or debonding from the matrix, was observed at the fracture surface of ICCGHAZ. The presence of necklace type M-A constituent in ICCGHAZ notably increases the susceptibility of cleavage microcrack nucleation. Furthermore, the study of secondary microcracks beneath the CGHAZ and the ICCGHAZ through EBSD suggested that the fracture mechanism changes from nucleation-controlled in the CGHAZ to propagation-controlled in the ICCGHAZ because of the presence of necklace-type M-A constituent in the ICCGHAZ region. Both fracture mechanism contribute to the poor toughness of the sample contained ICCGHAZ. In conclusion, big prior austenite grains with low density of HAB plus coarse necklacing M-A products along grain boundary is the dominant factor resulting in low toughness.