Kinetic Modeling of the Silicothermic Reduction of Manganese Oxide from Slag

A model was developed to describe the mixed rate control kinetics in systems with MnO-SiO2-CaO-Al2O3 slags and Fe-Si metal droplets. During the reaction of Fe-Si droplets and slag, Mn2+ transport was found to be part of controlling the system but could not sufficiently describe all initial conditions (chiefly, changes to initial silicon content). The current model describes the kinetics of the stated system and offers answers to the question of rate control; the model has been fitted to nine datasets of varying initial conditions including initial [Si], initial (MnO), initial droplet size, and reaction temperature. The fitted mass transfer coefficients for metal and slag were 2.3 × 10−4 and 6.7 × 10−4 m/s, respectively; these values are constant across the nine datasets. Previous claims about the efficiency of silicon usage in reducing manganese have been modified; it appears that the formation of silica is favored throughout the reaction, but that the formation of a silicon monoxide gas layer on the metal surface dramatically impacts the rate of reaction. As a measure of overall fit of the model, the average of the root-mean-square errors for all datasets is 14 pct. Mass transport in slag is twice as influential on rate control as the metal phase. The simultaneous transport of both Mn2+ and silicate dimers controls mass transport in the slag. Both [Si] and [Mn] can control from the metal side but are dependent on the initial conditions.