Reduction behaviour of rice husk ash for preparation of high purity silicon

The reduction of rice husk ash (RHA) silica for the preparation of high purity silicon was studied using magnesium as the reducing agent. Composite magnesium–RHA pellets with magnesium content varying 0–25 wt-% in excess of stoichiometry requirement were made and heated in the temperature range of 600–900°C under flowing argon. It was found through differential thermal analysis and temperature profile recording that the reaction of RHA silica with magnesium was triggered at ∼575°C. Quantitative X-ray diffraction analyses of the reduction products showed that both initial magnesium content of the pellets and the reduction dwell temperature had a significant influence on the yield of silicon. In this study, a charge with 5 wt-% magnesium in excess of the stoichiometric amount at a reduction temperature of 900°C gave a maximum silicon yield. On a étudié la réduction de la silice de cendre de balle de riz (RHA) dans la préparation de silicium à haut degré de pureté en utilisant du magnésium comme agent de réduction. On a fabriqué des boulettes composites de magnésium-RHA avec une teneur en magnésium variant de 0 à 25% en poids en excès des besoins de la stoechiométrie et on les a chauffées dans la gamme de température de 600 à 900°C sous un flux d’argon. On a trouvé, par analyse thermique différentielle (DTA) et par enregistrement du profil de température, que la réaction de la silice de RHA avec le magnésium était déclenchée à environ 575°C. Des analyses quantitatives par XRD des produits de réduction ont montré que tant la teneur initiale en magnésium des boulettes que la température de maintien de la réduction avaient une influence importante sur le rendement en silicium. Dans cette étude, une charge avec 5% en poids d’excès de magnésium sur la quantité stoechiométrique à la température de réduction de 900°C donnait un rendement maximal de silicium.