Investigating the Impact of Physical Vapour Deposition (PVD)-Coated Cutting Tools on Stress Corrosion Cracking Susceptibility in Turning Super Duplex Stainless Steel

This work aimed to ascertain the corresponding influences of several PVD-coated cutting tools on the susceptibility of the machined surface of super duplex stainless steel (SDSS) to stress corrosion cracking. Coatings comprised of AlCrN, AlCrN/TiSiN, and AlTiN were applied to cemented carbide cutting tools using the PVD method; these were then used to turn the outer surface of the SDSS tube section. During the cutting process, the material presents the following combination of features: (i) a tendency for strain hardening, reflected in microstructural modifications and residual stresses of the machined surface and (ii) high temperatures in the cutting region, reducing the tool life. The goal of this work was to evaluate the surface integrity (work hardening and corrosion behaviour) of the SDSS obtained after the machining process (finish turning) with cemented carbide tools coated with three different PVD coatings.