The Influence of Pressure on Fracture of a Ti-V Plate Steel

The effect of hydrostatic pressure on the fracture behaviour of a hot-rolled plate steel subjected to two different thermomechanical histories has been studied. The pressure-dependent ductility of the annealed plate was in good agreement with the results of a model based on void growth in a powerhardening solid. Both plates exhibited a transition from ductile fracture to shear fracture at a critical level of hydrostatic pressure; however, the plate with the lower finishing temperature exhibited the transition at lower levels of pressure and plastic strain. This behaviour can be rationalized in terms of the anisotropic plastic properties of the plate. Résumé L'effet de la compression hydrostatique sur le comportement en rupture d'une tôle d'acier laminée à chaud, ayant subi deux traitements thermomécaniques différents a été étudié. La dépendance de la ductilité envers la pression, pour la tôle recuite, est en accord avec les résultats issus d'un modèle de croissance de cupules au sein d'un solide dont la consolidation suit une loi de puissance. Les deux tôles démontrent une transition entre un mode de rupture ductile et un mode de rupture par cisaillement lorsqu'un seuil critique de compression hydrostatique est atteint. Toutefois, celle dont la température de finition est la plus basse démontre une transition vers de plus faib1es valeurs de pression et déformation plastique. Un tel comportement peut être expliqué par l'anisotropie des propriétés de plasticité de la tôle.