Investigations on nylon 4 membranes: Synthesis and transport properties. II. Transport properties of nylon 4 polymer membranes

AbstractThe reverse osmosis, ultrafiltration, and dialysis properties of nylon 4 membranes to separations of sodium chloride, urea, a series of ethylene glycols and other compounds in the aqueous phase were investigated. The nylon 4 membranes were prepared from a formic acid solution with and without organic or inorganic additives. The effects of polymer concentration, amount of additives, casting time, and temperature on the membrane performance in terms of salt separation and product rate were investigated. The tensile properties of the nylon 4 membranes in both the dry and wet states were determined. It was found that the highest salt separation of a 0.1% sodium chloride solution did not exceed 53.3%. However, these membranes showed some intersting dialysis properties which were comparable to those of commercial cellophane and cellulose acetate membranes.

Investigations on nylon 4 membranes: Synthesis and transport properties. II. Transport properties of nylon 4 polymer membranes Journal Articles