ELECTRIC ARC FURNACE DUST INJECTION INTO IRON AND STEEL MELTS

The dust generated during electric arc furnace (EAF) steelmaking contains zinc and lead. The dust can be injected into the furnace to enhance the zinc and lead grades in the dust; however, the kinetics of this operation is poorly understood. The kinetics was studied in experiments in which dust was injected into 70 kg heats of iron or steel in an induction furnace. Supplemental additions of carbon and oxygen to overcome the heat load on the system were also investigated. The zinc content increased from 16% Zn to 60 - 80% Zn. About 50% of the zinc in the dust dissolved in the iron or steel. The ZnO in the dust is shown to be reduced by dissolved carbon and the zinc vapour dissolved in the iron. The implications for EAF dust recycling are discussed. La poussière engendrée lors de la production d’acier dans un four à arc électrique contient du zinc et du plomb. On peut injecter la poussière dans le four pour améliorer la qualité du zinc et du plomb dans la poussière; cependant, la cinétique de cette opération est mal comprise. On a étudié la cinétique au cours d’expériences dans lesquelles on injectait la poussière dans des coulées de 70 kg de fer ou d’acier dans un four à induction. On a également étudié des additions supplémentaires de carbone et d’oxygène pour surmonter la charge calorifique sur le système. La teneur en zinc a augmenté de 16% Zn à 60-80% Zn. Approximativement 50% du zinc dans la poussière s’est dissous dans le fer ou l’acier. On a montré que le ZnO présent dans la poussière était réduit par le carbone dissous et par la vapeur de zinc dissoute dans le fer. On discute des implications pour le recyclage de la poussière de four à arc électrique.