Effect of hydrogen passivation on the photoluminescence of Tb ions in silicon rich silicon oxide films

In this work, silicon-rich silicon oxide films containing terbium were prepared by means of plasma enhanced chemical vapor deposition. The influence of hydrogen passivation on defects-mediated non-radiative recombination of excited Tb3+ ions was investigated by photoluminescence, photoluminescence excitation, and photoluminescence decay measurements. Passivation was found to have no effect on shape and spectral position of the excitation spectra. In contrast, a gradual increase in photoluminescence intensity and photoluminescence decay time was observed upon passivation for the main 5D4-7F5 transition of Tb3+ ions. This observation was attributed to passivation of non-radiative recombination defects centers with hydrogen. It was found that the number of emitted photons increases upon passivation as a result of two effects: (1) longer Tb3+ lifetime in the 5D4 excited state and (2) optical activation of new Tb3+ emitters. The obtained results were discussed and compared with other experimental reports.

Effect of hydrogen passivation on the photoluminescence of Tb ions in silicon rich silicon oxide films Journal Articles