Electrical Conductivity and Thermal Expansion of Spinels at Elevated Temperatures Journal Articles uri icon

  •  
  • Overview
  •  
  • Research
  •  
  • Identity
  •  
  • Additional Document Info
  •  
  • View All
  •  

abstract

  • Binary oxide spinels composed of Mg, Al, Cr, Mn, Fe, Co, Ni, Cu, and Zn were synthesized. Electrical conductivity was measured in air at 500°–800°C. Thermal expansion was measured from room temperature to 1000°C. Ferrite spinels have thermal expansion coefficients of 11–12 ppm/K, compared with 7–9 ppm/K for other spinels except Cu–Mn and Co–Mn which show anomalous behavior. The highest electrical conductivity among transition metal spinels was found for MnCo2O4 (60 S/cm at 800°C) and Cu1.3Mn1.7O4 (225 S/cm at 750°C).

publication date

  • May 2007